High Chromium Grinding Ball

High chromium grinding balls typically have better corrosion resistance, especially in environments with high humidity or conditions containing corrosive substances. This helps reduce damage caused by corrosion and extends the lifespan of the steel balls. The manufacturing process of High chromium grinding balls is more refined, ensuring that the performance of each ball remains highly consistent, providing more stable operational performance.

Contact Now E-Mail Telephone WhatsApp

Product Details

Introduction of the product

High chromium grinding balls generally offer enhanced corrosion resistance, particularly in environments with high humidity or in conditions with corrosive materials. This reduces corrosion-related damage and prolongs the service life of the balls. The production process of high chromium grinding balls is more precise, ensuring that each ball's performance remains consistent, which results in more reliable and stable operation.

Application in grinding machines and areas

Machines	Industries
·Ball mills	·Mining industry
·SAG mills	·Power stations
·Tower mills	·Cement industry
·Coal grinding machine	·Steel Industry
·Bearing	·Chemical Industry
	·Metallurgical industry

Technical data

Chemical Composition (%)
Name		C	Si	Mn	Cr	Mo	S	P	Cu	Ni
High Chromium Alloy Cast Balls	ZQCr26	2.0-3.3	≤1.2	0.3-1.5	23.0-30.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr20	2.0-3.3	≤1.2	0.3-1.5	18.0-23.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr15	2.0-3.3	≤1.2	0.3-1.5	14.0-18.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr12	2.0-3.3	≤1.2	0.3-1.5	10.0-14.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
Middle Chromium Alloy Cast Balls	ZQCr8	2.1-3.3	≤2.2	0.3-1.5	7.0-10.0	0-1.0	≤0.06	≤0.10	0-0.8	-
Middle Chromium Alloy Cast Balls	ZQCr5	2.1-3.3	≤1.5	0.3-1.5	4.0-6.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Low Chromium Alloy Cast Balls	ZQCr2	2.1-3.6	≤1.5	0.3-1.5	1.0-3.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Bainite Alloy Cast Balls	ZQQTB	3.2-3.8	2.0-3.5	2.0-3.0	-	-	≤0.03	≤0.10	-	-
Bainite Alloy Cast Balls	ZQQTM	3.2-3.8	2.0-3.5	0.5-1.5	-	-	≤0.03	≤0.10	-	-

Physical Features
Name		Surface Hardness (HRC)	Impact Value (J/cm²)	Breakage Rate (%)	Diameter Tolerance (mm)	Diameter (mm)	Drop Test (Times)
High Chromium Alloy Cast Balls	ZQCr26	≥58	≥4J	≤1.0	Φ≤30 +1.0 -1.0 30＜Φ≤60 ＋1.5 -1.0 60＜Φ≤80 +2.0 -1.0 80＜Φ≤100 +2.5 -1.0 Φ＞100 +3.0 -1.0	10-160	＞15000
	ZQCr20	≥58	≥4J	≤1.0
	ZQCr15	≥58	≥4J	≤1.0
	ZQCr12	≥58	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr8	≥48	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr5	≥47	≥4J	≤1.0
Low Chromium Alloy Cast Balls	ZQCr2	≥45	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTB	≥50	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTM	≥52	≥4J	≤1.0

Quality Control Technology and Equipment

Plants and Production Equipment

Plants and Production Equipment

Exhibitions

Exhibitions

Why choose us

Reduce breakage rate: High chromium steel balls, with their superior impact resistance and wear resistance, effectively minimize breakage and fracture, ensuring more stable performance. This is crucial for equipment and production lines that demand high durability. Enhance impact resistance: High chromium steel balls are highly resistant to intense impact, especially in heavy-duty and high-impact environments, offering better performance compared to standard steel balls.