10-32%Cr Cast Grinding Ball

The 10-32% Cr Cast Grinding Ball is engineered for exceptional durability, offering a long service life even in the most demanding grinding environments. With chromium content ranging from 10% to 32%, these balls exhibit remarkable resistance to wear and corrosion, significantly reducing the need for frequent replacements. Their high strength and toughness ensure they maintain their integrity under high impact and pressure, making them an ideal choice for heavy-duty mining and industrial grinding applications.

Contact Now E-Mail Telephone WhatsApp

Product Details

Introduction of the product

Thanks to its precise manufacturing process, the 10-32% Cr Cast Grinding Ball ensures efficient grinding performance. The uniform hardness and optimal surface finish of these balls allow for consistent grinding, improving productivity while reducing energy consumption. Their ability to deliver fine, uniform results makes them a valuable asset in both coarse and fine grinding applications. Whether for mineral processing or cement industries, these balls help achieve optimal results, contributing to better operational efficiency.

Application in grinding machines and areas

Machines	Industries
·Ball mills	·Mining industry
·SAG mills	·Power stations
·Tower mills	·Cement industry
·Coal grinding machine	·Steel Industry
·Bearing	·Chemical Industry
	·Metallurgical industry

Technical data

Chemical Composition (%)
Name		C	Si	Mn	Cr	Mo	S	P	Cu	Ni
High Chromium Alloy Cast Balls	ZQCr26	2.0-3.3	≤1.2	0.3-1.5	23.0-30.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr20	2.0-3.3	≤1.2	0.3-1.5	18.0-23.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr15	2.0-3.3	≤1.2	0.3-1.5	14.0-18.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr12	2.0-3.3	≤1.2	0.3-1.5	10.0-14.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
Middle Chromium Alloy Cast Balls	ZQCr8	2.1-3.3	≤2.2	0.3-1.5	7.0-10.0	0-1.0	≤0.06	≤0.10	0-0.8	-
Middle Chromium Alloy Cast Balls	ZQCr5	2.1-3.3	≤1.5	0.3-1.5	4.0-6.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Low Chromium Alloy Cast Balls	ZQCr2	2.1-3.6	≤1.5	0.3-1.5	1.0-3.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Bainite Alloy Cast Balls	ZQQTB	3.2-3.8	2.0-3.5	2.0-3.0	-	-	≤0.03	≤0.10	-	-
Bainite Alloy Cast Balls	ZQQTM	3.2-3.8	2.0-3.5	0.5-1.5	-	-	≤0.03	≤0.10	-	-

Physical Features
Name		Surface Hardness (HRC)	Impact Value (J/cm²)	Breakage Rate (%)	Diameter Tolerance (mm)	Diameter (mm)	Drop Test (Times)
High Chromium Alloy Cast Balls	ZQCr26	≥58	≥4J	≤1.0	Φ≤30 +1.0 -1.0 30＜Φ≤60 ＋1.5 -1.0 60＜Φ≤80 +2.0 -1.0 80＜Φ≤100 +2.5 -1.0 Φ＞100 +3.0 -1.0	10-160	＞15000
	ZQCr20	≥58	≥4J	≤1.0
	ZQCr15	≥58	≥4J	≤1.0
	ZQCr12	≥58	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr8	≥48	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr5	≥47	≥4J	≤1.0
Low Chromium Alloy Cast Balls	ZQCr2	≥45	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTB	≥50	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTM	≥52	≥4J	≤1.0

Quality Control Technology and Equipment

Plants and Production Equipment

Plants and Production Equipment

Exhibitions

Exhibitions

Why choose us

The 10-32% Cr Cast Grinding Ball can be customized to meet the specific needs of different grinding processes. With a range of chromium content options, these balls can be tailored to enhance performance in particular mining or milling conditions. Whether you require balls with higher abrasion resistance or need a specific size, the flexibility of customization ensures that your grinding needs are precisely met, maximizing efficiency and cost-effectiveness

Leave your messages