Low Chromium Alloy Casting Balls

Low Chromium Alloy Casting Balls offer a cost-effective solution for industries that require high-quality grinding media but at a lower price point. These balls are made from an alloy with a controlled low chromium content, which balances wear resistance and cost efficiency. The lower chromium content provides sufficient hardness and durability for grinding softer to medium materials while keeping production costs under control. For industries like mining, cement, and chemical processing, Low Chromium Alloy Casting Balls represent an excellent value without compromising on performance.

Contact Now E-Mail Telephone WhatsApp

Product Details

Introduction of the product

Low Chromium Alloy Casting Balls provide a longer service life compared to standard carbon steel balls, thanks to their carefully engineered alloy composition. These balls are designed to withstand moderate grinding conditions and offer superior resistance to wear compared to conventional grinding media. The excellent combination of performance and affordability makes Low Chromium Alloy Casting Balls a preferred choice for companies that need effective grinding solutions while keeping costs low. Their longer lifespan means reduced downtime and maintenance, leading to more efficient operations and reduced operational costs.

Application in grinding machines and areas

Machines	Industries
·Ball mills	·Mining industry
·SAG mills	·Power stations
·Tower mills	·Cement industry
·Coal grinding machine	·Steel Industry
·Bearing	·Chemical Industry
	·Metallurgical industry

Technical data

Chemical Composition (%)
Name		C	Si	Mn	Cr	Mo	S	P	Cu	Ni
High Chromium Alloy Cast Balls	ZQCr26	2.0-3.3	≤1.2	0.3-1.5	23.0-30.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr20	2.0-3.3	≤1.2	0.3-1.5	18.0-23.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr15	2.0-3.3	≤1.2	0.3-1.5	14.0-18.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
	ZQCr12	2.0-3.3	≤1.2	0.3-1.5	10.0-14.0	0-3.0	≤0.06	≤0.10	0-1.2	0-1.5
Middle Chromium Alloy Cast Balls	ZQCr8	2.1-3.3	≤2.2	0.3-1.5	7.0-10.0	0-1.0	≤0.06	≤0.10	0-0.8	-
Middle Chromium Alloy Cast Balls	ZQCr5	2.1-3.3	≤1.5	0.3-1.5	4.0-6.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Low Chromium Alloy Cast Balls	ZQCr2	2.1-3.6	≤1.5	0.3-1.5	1.0-3.0	0-1.0	≤0.10	≤0.10	0-0.8	-
Bainite Alloy Cast Balls	ZQQTB	3.2-3.8	2.0-3.5	2.0-3.0	-	-	≤0.03	≤0.10	-	-
Bainite Alloy Cast Balls	ZQQTM	3.2-3.8	2.0-3.5	0.5-1.5	-	-	≤0.03	≤0.10	-	-

Physical Features
Name		Surface Hardness (HRC)	Impact Value (J/cm²)	Breakage Rate (%)	Diameter Tolerance (mm)	Diameter (mm)	Drop Test (Times)
High Chromium Alloy Cast Balls	ZQCr26	≥58	≥4J	≤1.0	Φ≤30 +1.0 -1.0 30＜Φ≤60 ＋1.5 -1.0 60＜Φ≤80 +2.0 -1.0 80＜Φ≤100 +2.5 -1.0 Φ＞100 +3.0 -1.0	10-160	＞15000
	ZQCr20	≥58	≥4J	≤1.0
	ZQCr15	≥58	≥4J	≤1.0
	ZQCr12	≥58	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr8	≥48	≥4J	≤1.0
Middle Chromium Alloy Cast Balls	ZQCr5	≥47	≥4J	≤1.0
Low Chromium Alloy Cast Balls	ZQCr2	≥45	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTB	≥50	≥4J	≤1.0
Bainite Alloy Cast Balls	ZQQTM	≥52	≥4J	≤1.0

Quality Control Technology and Equipment

Plants and Production Equipment

Plants and Production Equipment

Exhibitions

Exhibitions

Why choose us

The Low Chromium Alloy Casting Balls are specifically designed for applications that involve medium-impact grinding conditions. While they do not offer the extreme wear resistance of higher chromium balls, they still maintain a good level of hardness and durability for less demanding grinding operations. Their wear resistance makes them well-suited for industries that deal with softer or less abrasive materials, offering a good balance between performance and cost. The reliability of Low Chromium Alloy Casting Balls ensures smooth grinding processes while minimizing the need for frequent replacements.