Hot Rolled Grinding Ball

Hot rolled grinding ball process enhances the strength and hardness of the steel balls, enabling them to withstand extreme operating conditions. Although hot rolled steel balls have a higher initial cost compared to cast steel balls, their longer service life and reduced replacement needs make them more cost-effective in the long run. These advantages make hot rolled steel balls the preferred choice for industries requiring high-performance grinding media.

Contact Now E-Mail Telephone WhatsApp

Product Details

Hot rolled grinding ball Product Details

Although the initial investment in hot rolled steel balls is higher, their longer service life and lower replacement costs can significantly reduce overall operational costs in the long run, enhancing the economic efficiency of the business.

Hot Rolled Grinding Ball

Application in grinding machines and areas

Machines	Industries
·Ball mills	·Mining industry
·SAG mills	·Power stations
·Tower mills	·Cement industry
·Coal grinding machine	·Steel Industry
·Bearing	·Chemical Industry
	·Metallurgical industry

Technical data

Chemical Composition (%)
Steel Specification	C	Mn	Si	Cr	S	P
40Cr	0.37-0.44	0.50-0.80	0.17-0.37	0.80-1.15	≤0.035	≤0.035
42CrMo	0.38-0.45	0.50-0.80	0.17-0.37	0.90-1.25	≤0.035	≤0.035
60Mn	0.57-0.65	0.70-1.00	0.17-0.37	≤0.25	≤0.035	≤0.035
65Mn	0.62-0.72	0.90-1.20	0.17-0.37	≤0.25	≤0.035	≤0.035
#45/C45	0.42-0.54	0.50-0.80	0.17-0.37	≤0.15	≤0.035	≤0.035
ZT-10	0.60-0.78	0.65-1.33	0.25-0.65	≤0.45	≤0.035	≤0.035
B2	0.70-0.92	0.70-1.00	0.17-0.37	0.40-0.70	≤0.035	≤0.035
B3	0.52-0.65	0.66-1.00	1.30-1.90	0.74-1.20	≤0.030	≤0.030
B4	0.65-0.75	0.50-0.70	1.20-1.40	0.85-1.00	≤0.025	≤0.025
B6	0.75-0.90	0.80-1.02	0.17-0.37	0.88-0.98	≤0.035	≤0.035
BU	0.95-1.05	0.95-1.05	0.15-0.35	0.45-0.55	≤0.035	≤0.035
BL	0.55-0.75	0.65-0.85	0.15-0.35	0.70-1.20	≤0.035	≤0.035
BG	0.90-1.05	0.35-0.95	0.15-0.35	1.00-1.70	≤0.035	≤0.035

Physical Features
Diameter (mm) (inches)	Surface Hardness (HRC)	Diameter Tolerance (mm)	Impact Value (J/cm²)	Breakage Rate (%)	Drop Test (times)
20 (0.79)	>60	+2.0 -1.0	≥12	≤1	>15000
25 (0.98)
30 (1.18)
40 (1.57)
50 (1.97)
60 (2.36)		+3.0 -1.5
65(5.56)
70 (2.76)
75 (3.00)
80 (3.15)
90 (3.54)
100 (3.94)		+4.0 -2.0
120 (4.72)	>58
125 (4.92)
140 (5.51)	>55	+5.0 -3.0
150 (5.91)

Quality Control Technology and Equipment

Plants and Production Equipment

Plants and Production Equipment

Exhibitions

Exhibitions

Why choose us

Due to their strong resistance to wear and tear, hot rolled steel balls reduce the need for maintenance and replacement of milling equipment during long-term use, lowering the complexity and cost of equipment maintenance. Hot rolled steel balls are more wear-resistant under high-impact and high-friction conditions, making them ideal for heavy-duty applications, such as grinding in ball mills.